OK 68.15 is a stainless-steel electrode which deposits a ferritic 13Cr weld metal. OK 68.15 is designed for welding steels of similar composition, when CrNi-alloyed austenitic stainless steel electrodes cannot be used, e.g. when the structure is going to be exposed to aggressive sulphuric gases. Depending on the welding parameters, the structure and consequently the mechanical properties of untreated weld metal can vary within fairly large limits.
Propiedades típicas de Tensión
| Condición | Gas de protección | Temperatura de prueba | Tiempo de prueba | Alargamiento | Límite de flujo | Resistencia a la tracción |
| Stress Relieved | AWS | 750 °C | 6 hr | – | – | – |
| Stress Relieved | AWS | 750 °C | 1 hr | 25 % | 370 MPa | 520 MPa |
Teste Charpy
| Condición | Gas de protección | Temperatura de prueba | Test Condition Temp | Test Condition Time | Valor de impacto |
| Stress Relieved | AWS | 20 °C | 750 | 6 | 55 J |
| Stress Relieved | AWS | 0 °C | 750 | 6 | 35 J |
| Stress Relieved | AWS | -20 °C | 750 | 6 | 20 J |
Composición química
| weld metal analysis | ||||
| Mn | C | Si | Ni | Cr |
| 0.3 % | 0.04 % | 0.4 % | 0.1 % | 12.9 % |
Depósito
| Cantidad de electrodos / kg de metal de soldadura | Corriente | Diámetro | Kg de soldadura metal / kg electrodos | Tasa de Deposición | Tensión | Tiempo de fusión por electrodo al 90% I max |
| 73 | 65-115 A | 2.5 x 350 mm | 0.62 kg | 1.0 kg/h | 25 V | 48 sec |
| 33 | 90-160 A | 3.2 x 450 mm | 0.63 kg | 1.5 kg/h | 25 V | 71 sec |
| 24 | 120-220 A | 4.0 x 450 mm | 0.57 kg | 2.0 kg/h | 30 V | 73 sec |
| Aprobaciones: | Seproz; UNA 272580 |
| Clasificaciones: | EN 14700; E Fe7; EN ISO 3581-A; E 13 B 4 2; SFA/AWS A5.4; E410-15; Werkstoffnummer; 1.4009 |
Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.
| Corriente de soldadura: | DC+ |
| tipo de aleación: | 13% Cr |
| Tipo de revestimiento: | Lime Basic |