OK Autrod 309LSI

A continous solid corrosion resistant chromium-nickel wire for welding of similar steels, wrought and cast steels of 23% Cr-12% Ni types. The alloy is also used for welding of buffer layers on CMn steels and welding of dissimilar joints. When using the wire for buffer layers and dissimilar joints it is necessary to control the dilution of the weld. OK Autrod 309LSi has a good general corrosion resistance. The higher silicon content improves the welding properties, such as wetting.

Descripción

Propiedades típicas de Tensión

As welded
Alargamiento Límite de flujo Resistencia a la tracción
41 % 440 MPa 600 MPa

Teste Charpy

Condición Temperatura de prueba Valor de impacto
As Welded 20 °C 160 J
As Welded -60 °C 130 J
As Welded -110 °C 90 J

Composición química

wire composition
Mn Mo Cu C Si Ni Cr
1.7 % 0.15 % 0.12 % 0.02 % 0.9 % 13.5 % 23.4 %

Depósito

Corriente Diámetro Tasa de Deposición Tensión Velocidad de Alimentación
55-160 A 0.8 mm 1.0-4.1 kg/h 15-24 V 4.0-17.0 m/min
65-220 A 0.9 mm 1.1-5.4 kg/h 15-28 V 3.5-18.0 m/min
80-240 A 1.0 mm 1.5-6.0 kg/h 15-28 V 4.0-16.0 m/min
1.14 mm
100-300 A 1.2 mm 1.6-7.5 kg/h 15-29 V 3.0-14.0 m/min
230-375 A 1.6 mm 5.2-8.6 kg/h 23-31 V 5.5-9.0 m/min

Aprobaciones: CE; EN 13479; CWB; ER309LSi; DB; 43.039.16; NAKS/HAKC; 1.0MM-1.2MM; VdTÜV; 10020
Clasificaciones: EN ISO 14343-A; G 23 12 L Si; Wire Electrode; SFA/AWS A5.9; ER309LSi; Wire Electrode; Werkstoffnummer; ~1.4332; Wire Electrode

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.

tipo de aleación: Austenitic (with approx. 8 % ferrite) 24 % Cr – 13 % Ni – Low C