OK Autrod 308LSI

A continuous solid corrosion resisting chromium-nickel wire for welding of austenitic chromium nickel alloys of 18% Cr – 8% Ni-type. OK Autrod 308LSi has a good general corrosion resistance. The alloy has a low carbon content making it particularly recommended where there is a risk of intergranular corrosion. The higher silicon content improves the welding properties, such as wetting. The alloy is widely used in the chemical and food processing industries as well as for pipes, tubes and boilers.

Descripción

Propiedades típicas de Tensión

As welded
Alargamiento Límite de flujo Resistencia a la tracción Gas de protección
36 % 400 MPa 570 MPa
25 % 370 MPa 490 MPa Tested at 350°C.

Teste Charpy

Condición Temperatura de prueba Valor de impacto
As Welded 20 °C 110 J
As Welded -60 °C 70 J
As Welded -196 °C 45 J

Composición química

wire composition
Mn Mo Cu C Si Ferrite FN Ni Cr
1.8 % 0.15 % 0.10 % 0.01 % 0.9 % 9 % 10.5 % 19.9 %

Depósito

Diámetro Corriente Tasa de Deposición Tensión Velocidad de Alimentación
0.6 mm
0.8 mm 55-160 A 1.0-4.1 kg/h 15-24 V 4.0-17.0 m/min
0.9 mm 65-220 A 1.1-5.4 kg/h 15-28 V 3.5-18.0 m/min
1.0 mm 80-240 A 1.5-6.0 kg/h 15-28 V 4.0-16.0 m/min
1.14 mm
1.2 mm 100-300 A 1.6-7.5 kg/h 15-29 V 3.0-14.0 m/min
1.6 mm 230-375 A 5.2-8.6 kg/h 23-29 V 5.5-9.0 m/min

 

Aprobaciones: BV; 308L SA BT (M12); CE; EN 13479; CWB; ER308LSi; DB; 43.039.01; DNV-GL; VL 308 L (M13); NAKS/HAKC; 0.8-1.2 mm; VdTÜV; 04267
Clasificaciones: EN ISO 14343-A; G 19 9 L Si; Wire Electrode; SFA/AWS A5.9; ER308LSi; Wire Electrode; Werkstoffnummer; ~1.4316; Wire Electrode

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.

 

tipo de aleación: Austenitic (with approx. 8 % ferrite) 19% Cr – 9% Ni – Low C – High Si