OK 68.15

OK 68.15 is a stainless-steel electrode which deposits a ferritic 13Cr weld metal. OK 68.15 is designed for welding steels of similar composition, when CrNi-alloyed austenitic stainless steel electrodes cannot be used, e.g. when the structure is going to be exposed to aggressive sulphuric gases. Depending on the welding parameters, the structure and consequently the mechanical properties of untreated weld metal can vary within fairly large limits.

Descripción

Propiedades típicas de Tensión

Condición Gas de protección Temperatura de prueba Tiempo de prueba Alargamiento Límite de flujo Resistencia a la tracción
Stress Relieved AWS 750 °C 6 hr
Stress Relieved AWS 750 °C 1 hr 25 % 370 MPa 520 MPa

Teste Charpy

Condición Gas de protección Temperatura de prueba Test Condition Temp Test Condition Time Valor de impacto
Stress Relieved AWS 20 °C 750 6 55 J
Stress Relieved AWS 0 °C 750 6 35 J
Stress Relieved AWS -20 °C 750 6 20 J

Composición química

weld metal analysis
Mn C Si Ni Cr
0.3 % 0.04 % 0.4 % 0.1 % 12.9 %

Depósito

Cantidad de electrodos / kg de metal de soldadura Corriente Diámetro Kg de soldadura metal / kg electrodos Tasa de Deposición Tensión Tiempo de fusión por electrodo al 90% I max
73 65-115 A 2.5 x 350 mm 0.62 kg 1.0 kg/h 25 V 48 sec
33 90-160 A 3.2 x 450 mm 0.63 kg 1.5 kg/h 25 V 71 sec
24 120-220 A 4.0 x 450 mm 0.57 kg 2.0 kg/h 30 V 73 sec

Aprobaciones: Seproz; UNA 272580
Clasificaciones: EN 14700; E Fe7; EN ISO 3581-A; E 13 B 4 2; SFA/AWS A5.4; E410-15; Werkstoffnummer; 1.4009

Aprobaciones vinculadas a la planta de producción. Para obtener más información, pongase en contacto con ESAB.

Corriente de soldadura: DC+
tipo de aleación: 13% Cr
Tipo de revestimiento: Lime Basic